| PROPERTY | VALUE | UNIT | TEST METHOD |
|---|---|---|---|
| MFI | 6 | g/10 min | D1238, 200ºC, 10kg |
| NI (Izod) | 17 | kg-cm/cm | D256, 1/4" at 23ºC |
| HDT | 75 | ºC | D648, 1/4" at 18.6 kg/cm² |
| HDT | 84 | ºC | D648, 1/4" at 4.6 kg/cm² |
| Flame Rating | V-0 (1.6) | Thickness : mm | UL-94 |
| PROPERTY | VALUE | UNIT | TEST METHOD |
|---|---|---|---|
| MFI | 30 | g/10 min | D1238, 200ºC, 10kg |
| NI (Izod) | 22 | kg-cm/cm | D256, 1/4" at 23ºC |
| HDT | 86 | ºC | D648, 1/4" at 18.6 kg/cm² |
| HDT | 94 | ºC | D648, 1/4" at 4.6 kg/cm² |
| Flame Rating | HB (1.5) | Thickness : mm | UL-94 |
| PROPERTY | VALUE | UNIT | TEST METHOD |
|---|---|---|---|
| MFI | 20 | g/10 min | D1238, 200ºC, 10kg |
| NI (Izod) | 27 | kg-cm/cm | D256, 1/4" at 23ºC |
| HDT | 87 | ºC | D648, 1/4" at 18.6 kg/cm² |
| HDT | 96 | ºC | D648, 1/4" at 4.6 kg/cm² |
| Flame Rating | HB (1.5) | Thickness : mm | UL-94 |
| PROPERTY | VALUE | UNIT | TEST METHOD |
|---|---|---|---|
| MFI | 6 | g/10 min | D1238, 200ºC, 10kg |
| NI (Izod) | 13 | kg-cm/cm | D256, 1/4" at 23ºC |
| HDT | 104 | ºC | D648, 1/4" at 18.6 kg/cm² |
| HDT | 114 | ºC | D648, 1/4" at 4.6 kg/cm² |
| Flame Rating | HB (1.5) | Thickness : mm | UL-94 |
| PROPERTY | VALUE | UNIT | TEST METHOD |
|---|---|---|---|
| MFI | 18 | g/10 min | D1238, 200ºC, 10kg |
| NI (Izod) | 34 | kg-cm/cm | D256, 1/4" at 23ºC |
| HDT | 84 | ºC | D648, 1/4" at 18.6 kg/cm² |
| HDT | 90 | ºC | D648, 1/4" at 4.6 kg/cm² |
| Flame Rating | HB (1.5) | Thickness : mm | UL-94 |
| PROPERTY | VALUE | UNIT | TEST METHOD |
|---|---|---|---|
| MFI | 17 | g/10 min | D1238, 200ºC, 10kg |
| NI (Izod) | 36 | kg-cm/cm | D256, 1/4" at 23ºC |
| HDT | 84 | ºC | D648, 1/4" at 18.6 kg/cm² |
| HDT | 90 | ºC | D648, 1/4" at 4.6 kg/cm² |
| Flame Rating | HB (1.5) | Thickness : mm | UL-94 |