PROPERTY | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Polymer Structure | Linear | - | - |
Styrene Content | 24 | % | Abbe's refractmeter |
SI Diblock Content | 67 | % | Converted by Gel permeation chromatography |
Solution Viscosity | 0.32 | Pa*s | Brookfield Viscometer (25wt%, solids toluene solution at 25°C) |
Melt Index | 20 | g/10min. | ASTM D-1238 (G Condition) |
Hardness | 34 | Shore A | ASTM D-2240 |
300% Modulus | 0.8 | MPa | ATSM D-638 (modified) |
Tensile Strenght | 5 | MPa | ATSM D-638 (modified) |
Elongation | 800 | % | ATSM D-638 (modified) |
PROPERTY | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Polymer Structure | Linear | - | - |
Styrene Content | 25 | % | Abbe's refractmeter |
SI Diblock Content | 17 | % | Converted by Gel permeation chromatography |
Solution Viscosity | 0.38 | Pa*s | Brookfield Viscometer (25wt%, solids toluene solution at 25°C) |
Melt Index | 11 | g/10min. | ASTM D-1238 (G Condition) |
Hardness | 54 | Shore A | ASTM D-2240 |
300% Modulus | 1.8 | MPa | ATSM D-638 (modified) |
Tensile Strenght | 23 | MPa | ATSM D-638 (modified) |
Elongation | 1100 | % | ATSM D-638 (modified) |
PROPERTY | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Polymer Structure | Asymmetric | - | - |
Styrene Content | 48 | % | Abbe's refractmeter |
SI Diblock Content | - | % | Converted by Gel permeation chromatography |
Solution Viscosity | 0.25 | Pa*s | Brookfield Viscometer (25wt%, solids toluene solution at 25°C) |
Melt Index | 14 | g/10min. | ASTM D-1238 (G Condition) |
Hardness | 65 | Shore A | ASTM D-2240 |
300% Modulus | 4 | MPa | ATSM D-638 (modified) |
Tensile Strenght | 11 | MPa | ATSM D-638 (modified) |
Elongation | 700 | % | ATSM D-638 (modified) |
PROPERTY | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Polymer Structure | Linear | - | - |
Styrene Content | 14 | % | Abbe's refractmeter |
SI Diblock Content | 26 | % | Converted by Gel permeation chromatography |
Solution Viscosity | 1.4 | Pa*s | Brookfield Viscometer (25wt%, solids toluene solution at 25°C) |
Melt Index | 10 | g/10min. | ASTM D-1238 (G Condition) |
Hardness | 33 | Shore A | ASTM D-2240 |
300% Modulus | 0.8 | MPa | ATSM D-638 (modified) |
Tensile Strenght | 19 | MPa | ATSM D-638 (modified) |
Elongation | 1400 | % | ATSM D-638 (modified) |
PROPERTY | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Polymer Structure | Linear | - | - |
Styrene Content | 16 | % | Abbe's refractmeter |
SI Diblock Content | 56 | % | Converted by Gel permeation chromatography |
Solution Viscosity | 0.81 | Pa*s | Brookfield Viscometer (25wt%, solids toluene solution at 25°C) |
Melt Index | 12 | g/10min. | ASTM D-1238 (G Condition) |
Hardness | 31 | Shore A | ASTM D-2240 |
300% Modulus | 0.5 | MPa | ATSM D-638 (modified) |
Tensile Strenght | 11 | MPa | ATSM D-638 (modified) |
Elongation | 1500 | % | ATSM D-638 (modified) |
PROPERTY | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Polymer Structure | Radial | - | - |
Styrene Content | 19 | % | Abbe's refractmeter |
SI Diblock Content | 30 | % | Converted by Gel permeation chromatography |
Solution Viscosity | 0.55 | Pa*s | Brookfield Viscometer (25wt%, solids toluene solution at 25°C) |
Melt Index | 15 | g/10min. | ASTM D-1238 (G Condition) |
Hardness | 44 | Shore A | ASTM D-2240 |
300% Modulus | 1.4 | MPa | ATSM D-638 (modified) |
Tensile Strenght | 13 | MPa | ATSM D-638 (modified) |
Elongation | 1100 | % | ATSM D-638 (modified) |
PROPERTY | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Styrene Content | 25 | % | Abbe's refractmeter |
SI Diblock Content | - | % | Converted by Gel permeation chromatography |
Solution Viscosity | 0.38 | Pa*s | Brookfield Viscometer (25wt%, solids toluene solution at 25°C) |
Melt Index | 11 | g/10min. | ASTM D-1238 (G Condition) |
Hardness | 55 | Shore A | ASTM D-2240 |
300% Modulus | 1.8 | MPa | ATSM D-638 (modified) |
Tensile Strenght | 6 | MPa | ATSM D-638 (modified) |
Elongation | 960 | % | ATSM D-638 (modified) |
PROPERTY | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Polymer Structure | Linear | - | - |
Styrene Content | 15 | % | Abbe's refractmeter |
SI Diblock Content | 78 | % | Converted by Gel permeation chromatography |
Solution Viscosity | 1.1 | Pa*s | Brookfield Viscometer (25wt%, solids toluene solution at 25°C) |
Melt Index | 7 | g/10min. | ASTM D-1238 (G Condition) |
Hardness | 21 | Shore A | ASTM D-2240 |
300% Modulus | 0.3 | MPa | ATSM D-638 (modified) |
Tensile Strenght | 2 | MPa | ATSM D-638 (modified) |
Elongation | 2000 | % | ATSM D-638 (modified) |
PROPERTY | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Polymer Structure | Hybrid (mix of Linear and Radial structure) | - | - |
Styrene Content | 14 | % | Abbe's refractmeter |
SI Diblock Content | 12 | % | Converted by Gel permeation chromatography |
Solution Viscosity | 1.5 | Pa*s | Brookfield Viscometer (25wt%, solids toluene solution at 25°C) |
Melt Index | 9 | g/10min. | ASTM D-1238 (G Condition) |
Hardness | 36 | Shore A | ASTM D-2240 |
300% Modulus | 0.9 | MPa | ATSM D-638 (modified) |
Tensile Strenght | 24 | MPa | ATSM D-638 (modified) |
Elongation | 1300 | % | ATSM D-638 (modified) |
PROPERTY | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Styrene Content | 14 | % | Abbe's refractmeter |
SI Diblock Content | - | % | Converted by Gel permeation chromatography |
Solution Viscosity | 1.5 | Pa*s | Brookfield Viscometer (25wt%, solids toluene solution at 25°C) |
Melt Index | 9 | g/10min. | ASTM D-1238 (G Condition) |
Hardness | 36 | Shore A | ASTM D-2240 |
300% Modulus | 0.9 | MPa | ATSM D-638 (modified) |
Tensile Strenght | 24 | MPa | ATSM D-638 (modified) |
Elongation | 1300 | % | ATSM D-638 (modified) |
PROPERTY | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Polymer Structure | Asymmetric | - | - |
Styrene Content | 30 | % | Abbe's refractmeter |
SI Diblock Content | 60 | % | Converted by Gel permeation chromatography |
Solution Viscosity | - | Pa*s | Brookfield Viscometer (25wt%, solids toluene solution at 25°C) |
Melt Index | 12 | g/10min. | ASTM D-1238 (G Condition) |
Hardness | 42 | Shore A | ASTM D-2240 |
300% Modulus | - | MPa | ATSM D-638 (modified) |
Tensile Strenght | - | MPa | ATSM D-638 (modified) |
Elongation | - | % | ATSM D-638 (modified) |